SPECIAL ZINC-RICH EPOXY PRIMER

Product Code: RTB-1180-R

Download:

TDS MSDS MSDS
Segment
Protective and Industrial
Type
Primer, Zinc-Rich Primer
Type of Binder
Epoxy
Application
Anti-Corrosive, Cathodic Protection, Coastal Environments, Corrosive Environments, Heavy Duty Protective Coatings, High-Build, Humid Environments, Immersion Service, Polluted Environments, Potable Water Tank Lining, Water Tank Lining, Weldable
Substrate
Metal, Steel

Special high-build, two-component Zinc-rich epoxy coating with excellent adhesion and anti-corrosive properties.

  • Recommended Uses
    Primer coat for steel structures, maintenance operations, and brushed or sandblasted steel surfaces.
    Suitable Top-Coats
    RTB-1180-R can be over-coated with all types of coatings and finishes.
  • Type of Binder
    Epoxy – Polyamide
    Number of Component(s)
    2 Components
    Curing Mechanism
    Chemical Reaction
    Solid Content After Mixing
    88 ± 1% By Weight
    65 ± 3 % By Volume
    Flash Point
    28°C (82°F)
    Main Pigment(s)
    Pure Metallic Zinc Powder
    Zinc Content in Dried Film
    80 ± 1% By Weight
  • Finish / Colour
    Flat | Grey
  • Packing
    Component A (Epoxy): 10 L|Component B (Hardener): 4 L
    Storage Conditions
    To be stored in cool and dry conditions in original sealed containers.
    Shelf Life
    At least 9 months after delivery.
    Safety
    This product contains organic solvents and flammable materials. Keep away from sparks, fires, electrical cables and equipment, direct sunshine and out of children’s reach.
    Protect skin, eyes, and avoid prolonged breathing of solvent vapor during application. Use with adequate ventilation .

Technical Support Procedures and Guides

Technical Guide/Procedure Code and Name Download
TP-9101-18 - Surface Preparation for Expired Recoating Interval
This procedure document provides guidelines and instructions to follow in the event that the recoating interval between the application of different layers has expired, helping to ensure that strong bonding between the layers is achieved.
TP-9102-18 - Repair and Touch-Up Procedures
This procedure document provides guidelines and instructions to follow when repairing and touching up coatings, helping to ensure a prolonged service life for coatings that may have been damaged during installation and pre-commissioning, or during their service life.
TG-9902-18 - Surface Preparation Guide
This guide compares typical surface preparation standards such as Swedish Standards (SIS-5900), National Association of Civil Engineers (N.A.C.E.), American Standards (SSPC), Japanese Standards (SPSS), and British Standards (BS-5934). This guide also explains typical surface preparation requirements for different substrates based on different applications.
TG-9903-18 - Effect of Ambient Conditions on Dew Point
This guide provides a reference table that shows the relationship between Dew Point and relative humidity and ambient temperature, as well as a formula to calculate Dew Point for other values.
TG-9904-18 - Airless and Conventional Spray Application Parameters
This guide provides general information on application parameters when using conventional and airless spray application systems.
TG-9905-18 - Correlation Between Wet and Dry Film Thickness
This guide provides a reference table that quickly converts Dry Film Thickness (DFT) requirements to West Film Thickness (WFT) requirements based on a coating's Solid Content percentage.